- Home
-
Products
- Wear Pipe And Elbow For Engineering Machinery Industry
- Wear Pipe And Elbow For Port Industry
- Wear Pipe And Elbow For Glass Industry
- Wear Pipe And Elbow For Iron And Steel Industry
- Wear Pipe And Elbow For Power Industry
- Wear Pipe And Elbow For Cement Industry
- Wear Pipe And Elbow For Mining Industry
- Wear Plate For Engineering Machinery Industry
- Wear Plate For Port Industry
- Wear Plate For Glass Industry
- Wear Plate For Iron And Steel Industry
- Wear Plate For Power Industry
- Wear Plate For Cement Industry
- Wear Plate For Mining Industry
- welding wire
- Wear Parts Rebuild And Manufacture
- Wear Component And Fabrication
- News
- Case
- Factory Show
- Contact Us
- About Us
What is the difference between bimetal wear-resistant steel plate and hardened wear-resistant steel plate?
2023-11-29 15:54
1. Definition:
⑴Bimetal wear-resistant steel platerefers to the composite high-alloy wear-resistant layer on the substrate of ordinary steel plate by hardfacing method, combining the wear-resistant performance of the wear-resistant layer and the load-bearing, deformability and weldability of the substrate. The hardness of the wear-resistant layer is generally between HRC52-64.
⑵ Hardened wear-resistant steel plate refers to a low-alloy steel plate that is hardened by quenching during the rolling process or the low-alloy steel plate is heat-treated and quenched and hardened. The hardness is generally HB350-500.
2. wear resistance and mechanism
The wear-resistant layer of the bimetal wear-resistant steel plate is a high-alloy component. There are a large number of high-hardness alloy carbides (about HV1600) embedded in the matrix in the metallographic structure, which are the main carbides that play a role in anti-wear. The actual micro hardness of the wear layer is much higher than the measured macro hardness. The strengthening method is the same as that of cemented carbide.
Hardened wear-resistant steel plate is quenched and hardened as a whole, and there is martensite in the metallographic structure to increase the overall hardness, and the micro-hardness and macro-hardness are basically the same.
Everyone is familiar with the two materials used for tools: cemented carbide and T10. Even if the macroscopic hardness of the quenched T12 steel and cemented carbide is basically the same, the wear resistance of cemented carbide is much higher than that of T12 steel. The reason is that there are a lot of carbides in the cemented carbide.
3. Temperature resistance
The hardened wear-resistant steel plate will gradually lose its hardness when used at a temperature higher than 250℃, which greatly reduces the wear resistance. The welding process will also reduce the hardness near the weld;
The wear-resistant layer of the bimetal wear-resistant steel plateis of high alloy composition, and it has the effect of secondary hardening at a certain temperature, and it can generally work below 650°C.
4.Process performancec
Hardened wear-resistant steel plates can be punched mechanically, but bimetal wear-resistant steel plates cannot be punched mechanically.
5. comprehensive comparison
\ | Hardened wear-resistant steel plate | Bimetal wear-resistant steel plate |
Hardening method | Quench hardening
| Hardfacing wear-resistant alloy |
Alloying elements | Si and Mn | Cr, Mo, V and B etc. |
Hardness
| HB350-500 | HRC52-64 |
Wear resistance
| generally | very good |
Temperature resistance
| poor | excellent |
Corrosion resistance | same as ordinary steel plat | Good |
Machining by mechanical method | yes | no |
Cutting method | Flame cutting |
Plasma cutting
|
Processing performance | excellent | normal |
Get the latest price? We'll respond as soon as possible(within 12 hours)